| Parameter | Value acc. to Normative Document | Actual Value |
| Penetration, 0.1 mm @ 25°C, @ 0°C, min |
61-70 20 |
74 20 |
| Softening Point Ring&Ball, °C, min | 47 | 48 |
| Ductility, cm, min: @ 25°C @ 0°C |
55 3.5 |
90 3.5 |
| Breaking Point, °C, max | Minus 15 | Minus 17 |
| Flash Point at open cup, °C, min | 230 | 230 |
| Change of Softening Point after heating, °C, max | 5 | 5 |
| Penetration Index | from -1.0 to +1.0 | -0.4 |
RCP: 02 56120112
Report: Petroleum road viscous bitumen grade BND 60/90 meets the requirements GOST 22245-90 amended 1.
The bitumen adhesion with the reference limestone by sample № 2 according to GOST 11508 by method A is ensured by the production technology.
Testing laboratory accreditation certificate № РОСС RU.0001.22НФ51 dated 12.04.2010.
| Parameter | Value acc. to Normative Document | Actual Value |
| Penetration, 0.1 mm @ 25°C, @ 0°C, min |
91-130 28 |
119 48 |
| Softening Point Ring&Ball, °C, min | 43 | 47 |
| Ductility, cm, min: @ 25°C @ 0°C |
65 4.0 |
71 4.0 |
| Breaking Point, °C, max | Minus 15 | Minus 25 |
| Flash Point at open cup, °C, min | 230 | 270 |
| Change of Softening Point after heating, °C, max | 5 | 5 |
| Penetration Index | from -1.0 to +1.0 | 0.4 |
RCP: 02 56120112
Report: Petroleum road viscous bitumen grade BND 90/130 meets the requirements GOST 22245-90 amended 1.
| Parameter | Value acc. to Normative Document | Actual Value |
| Penetration, 0.1 mm @ 25°C, @ 0°C, min |
61-70 20 |
68 20 |
| Softening Point Ring&Ball, °C, min | 47 | 48 |
| Ductility, cm, min: @ 25°C @ 0°C |
55 3.5 |
90 3.5 |
| Breaking Point, °C, max | Minus 15 | Minus 17 |
| Flash Point at open cup, °C, min | 230 | 230 |
| Change of Softening Point after heating, °C, max | 5 | 5 |
| Penetration Index | from -1.0 to +1.0 | -0.4 |
RCP: 02 56120112
Report: Petroleum road viscous bitumen grade BND 60/70 meets the requirements GOST 22245-90 amended 1.
The bitumen adhesion with the reference limestone by sample № 2 according to GOST 11508 by method A is ensured by the production technology.
Testing laboratory accreditation certificate № РОСС RU.0001.22НФ51 dated 12.04.2010.
| Parameter | Value acc. to Normative Document | Actual Value |
| Penetration, 0.1 mm @ 25°C, @ 0°C, min |
71-100 20 |
83 20 |
| Softening Point Ring&Ball, °C, min | 47 | 48 |
| Ductility, cm, min: @ 25°C @ 0°C |
55 3.5 |
90 3.5 |
| Breaking Point, °C, max | Minus 15 | Minus 17 |
| Flash Point at open cup, °C, min | 230 | 230 |
| Change of Softening Point after heating, °C, max | 5 | 5 |
| Penetration Index | from -1.0 to +1.0 | -0.4 |
RCP: 02 56120112
Report: Petroleum road viscous bitumen grade BND 70/100 meets the requirements GOST 22245-90 amended 1.
The bitumen adhesion with the reference limestone by sample № 2 according to GOST 11508 by method A is ensured by the production technology.
Testing laboratory accreditation certificate № РОСС RU.0001.22НФ51 dated 12.04.2010.
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 45-80 |
| Softening,temperature, °С | EN 1427 | ≥ 55 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 2 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥235 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -15 |
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 45-80 |
| Softening,temperature, °С | EN 1427 | ≥ 65 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 3 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥ 220 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -15 |
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 65-105 |
| Softening,temperature, °С | EN 1427 | ≥ 60 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 1 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥ 220 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -15 |
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 65-105 |
| Softening,temperature, °С | EN 1427 | ≥ 65 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 3 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥ 220 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -20 |
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 75-130 |
| Softening,temperature, °С | EN 1427 | ≥ 55 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 2 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥ 220 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -22 |
| Parameter | Test method | Standard according to Normative documents |
| Needle penetration depth, 0.1 mm 25°С 0°С |
EN 1426 | 75-130 |
| Softening,temperature, °С | EN 1427 | ≥ 75 |
| Ducility under force (pulling force) 50mm/min, J/cm2 | EN 13589, EN 13703 |
≥ 2 at 5°С |
| Resistance to hardening - Mass change, % - Residual penetration, % - Softening temperature increase, °С |
EN 12607-1 | ≤ 0,5 ≥ 60 ≤ 8 |
| Flash point, °С | EN ISO 2592 | ≥ 220 |
| Elasticity at 25 °С | EN 13398 | ≥ 80 |
| Flash brittle point, °С, min | EN 12593 | ≤ -15 |